題名: Vibration Analysis of Tennis Racquet Composite Grips with Ratios of Carbon and Glass Fibres
作者: Chen, T. Y.;Chen, C. Y.;Lin, D. C.;Huang, C. F.
貢獻者: 體育學系
關鍵詞: racket;damping ratio;vibration;material
日期: 2000-06
上傳時間: 2012-05-10T04:13:05Z
出版者: The Chinese University of Hong Kong
摘要: The purpose of this study was to analyze the vibrations from different tennis racquet grip materials. For this study, five different kinds of tennis racquet grips were used. The materials in the actual grip were composed of a mixture of carbon fibre and glass fibre in the ratio of 10 to 0, 7 to 3, 5 to 5, 3 to 7, and 0 to 10. Two accelerometers and BioPAC system were used to acquire the vibrational signals. The results of this study indicated that the tennis racquet made of pure carbon fibre, had a higher damping ratio on the center and off-center impact. The damping ratio was significantly decreased as the content of glass fibre in the racquet was increased (p.05). However, the value of the integral power spectrum was significantly increased (p). Therefore, based on the vibrational analysis among the difference in material composition of tennis racquets, it concluded that increasing the content of glass fibre in the racquet would increase the load carried by the tennis player’s arm.
關聯: XVIII International Symposium on Biomechanics in Sports, Hong Kong, June 25-30, 2000: 630-632
顯示於類別:[體育學系] 會議論文


檔案 大小格式瀏覽次數
2070100516001.pdf129KbAdobe PDF684檢視/開啟



DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋