題名: Influences on optoelectronic properties of damp heat stability of AZO and GZO for thin film solar cells
作者: Yen, Wen-Tsai;Ke, Jia-Hong;Wang, Hsin-Jung;Lin, Yi- Cheng;Chiang, Jung-Lung
貢獻者: 機電工程系
關鍵詞: Damp heat;Optoelectronic;Pulsed DC magnetron sputtering;ZnO:Al;ZnO:Ga
日期: 2009-09
上傳時間: 2012-07-05T07:14:17Z
摘要: This study investigates the effects of damp heat stability on the optoelectronic properties of ZnO:Al (AZO) and ZnO:Ga(GZO) films with respect to thin-film solar cells. The lowest resistivities of AZO and GZO thin films are 8.2621×10-4 Ω-cm and 2.8561×10-4 Ω-cm, respectively. After damp heat testing for 999h, the resistivities of AZO and GZO thin film increase by 39.72% and 11.97%, respectively. XPS binding energy analysis shows that the AZO thin film has a higher O 1s spectrum than the GZO thin film. Thus, the carrier concentration of films decreases, as a higher binding energy is attributed to the chemisorbed oxygen atoms (O-). Experimental results show that after expousre to a damp heat test at 85℃ and 85% relative humidity for electrical, optical, structural, and morphological analysis, GZO films are more stable than AZO films.
關聯: The 2nd International Conference on Multi-functional Materials and Structures, China, October 9-12, 2009
顯示於類別:[機電工程學系] 會議論文

文件中的檔案:

檔案 大小格式瀏覽次數
2050100216009.pdf175KbAdobe PDF621檢視/開啟


在NCUEIR中所有的資料項目都受到原著作權保護.

 


DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋