題名: The Carrier Blocking Effect on 850 nm InAlGaAs/AlGaAs Vertical-cavity Surface-emitting Lasers
作者: Chang, Yi-An;Ko, Tsung-Hsine;Lai, Fang-I;Chen, Jun-Rong;Yu, Chun-Lung;Wu, I-Tsung;Kuo, Hao-Chung;Kuo, Yen-Kuang;Laih, Li-Wen;Laih, Li-Horng;Lu, Tin-Chang;Wang, Shing-Chung
貢獻者: 物理學系
日期: 2006-09
上傳時間: 2012-07-19T01:47:39Z
出版者: IOP Publishing
摘要: In this study, the carrier blocking effect on 850 nm InAlGaAs/AlGaAs vertical-cavity surface-emitting layers (VCSELs) was theoretically and experimentally investigated. By means of inserting a high-bandgap electron blocking layer, which was either 10 nm thick Al0.75Ga0.25As or 13 nm thick Al0.9Ga0.1As, on the p-side of a quantum-well active region, the laser output performance was theoretically found to be improved. VCSELs with and without an electron blocking layer were also experimentally demonstrated. It was found that the threshold current was reduced from 1.47 to 1.33 mA and the slope efficiency was increased from 0.37 to 0.53 mW mA−1 by inserting a 10 nm thick Al0.75Ga0.25As electron blocking layer. Also, the device became less sensitive to the device temperature, where the amount of increase in the threshold current at an elevated temperature of 95 °C was only 0.27 mA and the slope efficiency dropped by only 24.5%. A peak frequency response of nearly 9 GHz at 5 mA, measured from relative intensity noise (RIN), was obtained in these VCSEL devices.
關聯: Semiconductor Science and Technology, 21(10): 1488-1494
顯示於類別:[物理學系] 期刊論文