题名: Anisotropy of Magnetic Critical Current Density HgBa2CuO4+δ
作者: Usami, R.;Puznizk, R.;Kubota, H.;Liu, Chia-Jyi;Yamauchi, H.
贡献者: 物理學系
日期: 1994
上传时间: 2012-09-10T06:11:58Z
摘要: The anisotropy of magnetic critical current density in HgBa2CuO40 has been investigated. HgBa2CuO40 was synthesized from the mixed powders of HgO, BaO and CuO in evacuated quartz tube at 750 C for lh. As-prepared HgBa2CuO4 was annealed in flowing argon at 300!C for 6h. Pulverized sample was aligned by a magnetic field of 8T in resin. The U- loop measurements of magnetically aligned crystalline HgBa2CuO4d were performed at 4.2K. The width of hysteresis loop, M b in the a-b plane and Ac along the c-axis, were calculated. The anisotropy of the width of hysteresis loop was observed, 1 .6SIUcor b/Mcorcs3. 1 in magnetic field up to 9T. The critical current densities, Jcb in the a-b plane and Jcc along the c-axis, were determined. The Jcb at 4.2K in lT was found to be equal to 1 .6x106A/cm2.
關聯: Bulletin of The Electrotechnical Laboratory, 58(6): 89-92
显示于类别:[物理學系] 期刊論文

文件中的档案:

档案 大小格式浏览次数
2020200410062.pdf49KbAdobe PDF389检视/开启


在NCUEIR中所有的数据项都受到原著作权保护.

 

DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈