題名: Irreversibility Lines for HgBa2CuO4+δ with Different Oxygen Contents
作者: Usami, R.;kubota, H.;Puzniak, R.;Liu, Chia-Jyi;Yamauchi, H.
貢獻者: 物理學系
日期: 1994-12
上傳時間: 2012-09-10T06:12:32Z
出版者: Elsevier
摘要: Single phase HgBa2CuO4+δ samples were annealed in flowing oxygen gas or in flowing argon gas. Oxygen contents of both samples determined by iodometric titrations indicate that the samples annealed in oxygen gas and in argon gas were respectively in over-doped and in under-doped region. Both samples were respectively grain-aligned in magnetic fields. Hysteresis loops for grain-aligned over-doped and under-doped samples were measured in applied fields parallel and perpendicular to the c-axis. Region where irreversibility lines of over-doped sample was located was found to be higher than that of under-doped sample. Irreversibility line of over-doped sample was found to be higher than that of YBa2Cu3O6.6. Anisotropy of irreversibility lines of both samples were found to be smaller than that of Y-123 superconductors.
關聯: Physica C: Superconductivity, 235-240: 2759-2760