题名: Improvement of Thermoelectric Power Factor of Hydrothermally Prepared Bi0.5Sb1.5Te3 Compared to its Solvothermally Prepared Counterpart
作者: Liu, Chia-Jyi;Liu, Gao-Jhih;Tsao, Chun-Wei;Huang, Yo-Jhih
贡献者: 物理學系
关键词: Bismuth telluride alloy;Hydrothermal synthesis;Solvothermal synthesis;Power factor;Thermoelectrics
日期: 2009
上传时间: 2012-09-10T06:15:53Z
出版者: SpringerLink
摘要: We report on the successful hydrothermal synthesis of Bi0.5Sb1.5Te3, using
water as the solvent. The products of the hydrothermally prepared Bi0.5
Sb1.5Te3 were hexagonal platelets with edges of 200–1500 nm and thicknesses
of 30–50 nm. Both the Seebeck coefficient and electrical conductivity of the
hydrothermally prepared Bi0.5Sb1.5Te3 were larger than those of the solvothermally
prepared counterpart. Hall measurements of Bi0.5Sb1.5Te3 at room
temperature indicated that the charge carrier was p-type, with a carrier
concentration of 9.47 9 1018 cm 3 and 1.42 9 1019 cm 3 for the hydrothermally
prepared Bi0.5Sb1.5Te3 and solvothermally prepared sample, respectively.
The thermoelectric power factor at 290 K was 10.4 lW/cm K2 and
2.9 lW/cm K2 for the hydrothermally prepared Bi0.5Sb1.5Te3 and solvothermally
prepared sample, respectively.
關聯: J. Electronic Materials, 38(7): 1499-1503