題名: High-Tc Superconducting Joints for Ag-Clad Bi-2223 Tapes
作者: Chen, K.;Tai, C. H.;Horng, Lance
貢獻者: 物理學系
日期: 1996-04
上傳時間: 2013-02-05T02:17:20Z
出版者: THE PHYSICAL SOCIETY OF THE REPUBLIC Or� CHINA
摘要: A high-ir, superconducting tape joint between two Xg-clad 81-2223 tapes has been
fabricated and characterized. Two pre-sintered tapes with one side of the silver striped
were lapped and then wrapped by a silver foil. The complex was uniaxially pressed
and followed b\- appropriate sinterin, yr to form a high-�l; superconducting tape joint.
Transport critical current through the joint (icj) was determined at liquid nitrogen
temperature. It KS found that the ratio of critical currents through the joint to that of
the tape, I,j/I,, depended on the uniaxial pressure and the slntering conduction. For
a test sample, I,j/I, reached 99~. Persistent current loops formed by Bi-2223 tapes
have also been fabricated and tested. Joint resistance of a loop was determined 10 be
- 4 x lo-l3 R after the initial decay time of 2 minutes.
關聯: CHINESE JOURNAL OF PHYSICS, 34(2-II): 462-465