题名: Investigation on the Exchange Coupling Properties of Ring-Shaped MnIr/CoFe Bilayers
作者: Chen, C. C.;Shiao, M. H.;Lin, Y. C.;Tsai, H. M.;Kuo, C. Y.;Horng, Lance;Wu, J. C.;Isogami, S.;Tsunoda, M.;Takahashi, M.
贡献者: 物理學系
关键词: Alternating gradient magnetometer;Exchange coupling;Magnetic hysteresis;Rings
日期: 2011-03
上传时间: 2013-02-05T02:20:41Z
出版者: IEEE
摘要: In this study, the exchange coupling properties of submicron patterned Mnlr/CoFe bilayers with strong exchange coupling strength were investigated. The large area of 2.5 mm × 2.5 mm of submicron sized bilayer rings were fabricated by electron beam lithography and ion-milling processes. The clear variations of normalized magnetic hysteresis loops of patterned films are the degradation of pinned CoFe at the Mnlr/CoFe interfaces and the decrease of exchange bias field, comparing with sheet film. After post-field-annealing treatment, only the exchange field was improved. A magnetic tunnel junction ring with outer diameter/linewidth of 2/0.5 μm was constructed as well to further certify the speculations. The magnetoresistance loops of as-fabricated and post-field annealed MTJ ring revealed that the slightly improved magnetoresistance ratio and exchange field. These results were attributed to the rearrangement of distorted spins at the sample edges. However, in comparison with sheet film, the great degradation of magnetoresistance ratio of patterned device, without respect to as-fabricated or post-field annealed, was not retrieved, revealing that the futility of post-field-annealing treatment to the pinning portion of CoFe layer.
關聯: IEEE Trans. on Magnetics, 47(3): 620-623
显示于类别:[物理學系] 期刊論文