题名: Surface Analysis of (NH4)2Sx-treated InGaN using X-ray Photoelectron Spectroscopy
作者: Tsai, Chang-Da;Fu, Ching-Hung;Lin, Yow-Jon;Lee, Ching-Ting
贡献者: 光電科技研究所
关键词: Electron mobility;Electron traps;Grain boundaries;Organic semiconductors;Passivation;Plasma materials processing;Thin film transistors
日期: 1999-03
上传时间: 2013-10-02T08:35:23Z
出版者: Elsevier B. V.
摘要: We report the performance of InGaP/GaAs/InGaP metal–semiconductor–metal photodetectors (MSM-PD's) using indium–tin–oxide (ITO) as transparent and antireflection Schottky electrode. The dark current and photoresponsivity of about 60 pA (i.e. 2.4 μA cm−2) and 0.58 A W−1 at 5 V bias for a 50×50 μm2 photosensitive area with 2 μm fingers and spaces were measured. We demonstrated that the corresponding rise time, fall time, full width at half maximum and 3 dB bandwidth of temporal responses were 26.4, 134.6, 44.6 ps and 7.0 GHz, respectively. The results of InGaP/GaAs/InGaP MSM-PD's with an ITO Schottky electrode were compared to those of identical geometry devices fabricated with a Ti/Pt/Au Schottky electrode.
關聯: Solid-State Electronics, 43(3): 665-670