题名: Nonalloyed Ohmic Mechanism of TiN Interfacial Layer in Ti/Al Contacts to (NH4)�2Sx-treated n-type GaN Layers
作者: Lee, Ching-Ting;Lin, Yow-Jon;Lin, Chun-Hung
贡献者: 光電科技研究所
关键词: Aluminium;Titanium;Titanium compounds;Gallium compounds;Ohmic contacts;Semiconductor-metal boundaries;III-V semiconductors;X-ray photoelectron spectra;Core levels;Wide band gap semiconductors;Vacancies (crystal);Surface treatment;Work function
日期: 2002-10
上传时间: 2013-10-02T08:35:49Z
出版者: American Institute of Physics
摘要: We investigate the nonalloyed ohmic contact of Ti/Al contacts to (NH4)2Sx-treated n-type GaN layers using x-ray photoelectron spectroscopy analysis. The native oxide on the n-type GaN surface can be completely removed by (NH4)2Sx solution. The resultant Ga/N ratio was decreased. The deposited Ti is in intimate contact with the (NH4)2Sx-treated n-type GaN layer. As a result, the TiN interlayer, which has a low work function and low electrical resistivity, is formed easily. The nonalloyed ohmic mechanism results from the formation of a TiN interlayer and the creation of nitrogen vacancies due to the nitrogen outdiffusion from the n-type GaN layer. The nonalloyed ohmic behavior of the as-deposited Ti/Al contacts with (NH4)2Sx-treated GaN layer was associated with Al/Ti/TiN/n-type GaN.
關聯: Journal of Applied Physics, 92(7): 3825-3829