題名: Magnetic Domain Structure and Coercivity Distribution for Patterned DyFeCo Thin Films
作者: Ye, L. X.;Lee, J. M.;Wu, Jong-Ching;Wu, Te-Ho
貢獻者: 物理學系
關鍵詞: Coercivity;Domain;Magnetooptical;Microhysteresis
日期: 2005-02
上傳時間: 2014-06-06T07:18:23Z
出版者: IEEE
摘要: The coercivity of patterned magnetooptical (MO) thin film media is quite different from that of nonpatterned samples. During the demagnetization process, we observed the sample's magnetic domain motion and structures. It was quite obvious that the coercivity values in the hole regions are unlike those on the land regions for patterned magnetic materials. Nevertheless, it was not possible to compute coercivity of holes and land regions directly. In this study, we measured of microhysteresis curves at a patterned position while mapping coercivity distribution using a Kerr microscope. The submicrometer images of the remanent state of domain reversal patterns were observed using a magnetic force microscope.
關聯: IEEE Transactions on Magnetics, 41(2): 956-958
顯示於類別:[物理學系] 期刊論文