Title: The Ac Effect of Vortex Pinning in the Arrays of Defects Sites on Nb Films
Authors: Wu, T. C.;Horng, Lance;Wu, Jong-Ching;Hsiao, C. W.;Kolacek, Jan;Yang, T. J.
Contributors: 物理學系
Date: 2006
Issue Date: 2014-06-06T07:18:35Z
Publisher: American Institute of Physics
Abstract: Niobium thin films with spacing-graded array of submicrometer-scaled holes had been fabricated using electron beam lithography through a lift-off technique. The magnetoresistance measurements and current-voltage characteristics were carried out with the external magnetic field applied perpendicular to the film plane, in which commensurable effects were observed in both experiments. The magnetoresistance with positive/negative directions of dc current revealed identical curves except the dips at matching fields separated. Two distinct current-voltage curves, which resulted from the positive and negative applied current directions, respectively, were discerned when the external magnetic field was fixed at the matching field, which is believed to be due to asymmetry pinning potential in the spacing-graded array of holes. In addition, ac current-voltage curve measured at matching field showed a ratchet bump along with another extra peak associated with incommensurable effect.
Relation: Journal of Applied Physics, 99(8): 08M515
Appears in Collections:[物理學系] 期刊論文

Files in This Item:

File SizeFormat

All items in NCUEIR are protected by copyright, with all rights reserved.


DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback