題名: Perpendicular Magnetic Tunneling Junction With Double Barrier Layers for MRAM Application
作者: A. Canizo Cabrera;Chang, Che-Hao;Hsu, Chih-Cheng;Weng, Ming-Chi;Chen, C. C.;Chao, C. T.;Wu, Jong-Ching;Chang, Yang-Hua;Wu, Te-Ho
貢獻者: 物理學系
關鍵詞: Magnetic tunneling junction (MTJ);Magnetoresistance (MR)
日期: 2007-02
上傳時間: 2014-06-06T07:18:43Z
出版者: IEEE
摘要: A double-barrier-layer perpendicular magnetic tunneling junction (DpMTJ) structure consisting of Si substrate/Pt/GdFeCo/AlOx/GdFeCo/FeCo/AlOx/FeCo/TbFeCo/Pt/Ti-cap was prepared by a direct current (dc) and radio frequency (RF) magnetron sputtering method. An elliptical DpMTJ element with 3.5 mumtimes2.5 mum size was fabricated using a top-down technique. A conducting atomic force microscope (CAFM) was used to obtain I-V curves of DpMTJ structures. We obtained the magnetoresistance (MR) ratio value from measured I-V curves by applying two opposite magnetic fields value of plusmn200 Oe perpendicular to the plane of film. The MR ratio was reached as high as 74% at zero applied bias voltage. Furthermore, the MR ratio decreased as bias voltage increased. It could make the DpMTJ structure to be used in the high-density MRAM devices
關聯: IEEE Transactions on Magnetics, 43(2): 914-916